POM 500 美国杜邦 物性参数表

文章出处:网络转载网责任编辑:admin人气:-发表时间:2016-01-07 16:46

POM 500 美国杜邦物性表

 

牌号500
厂家(产地)美国杜邦
规格级别注塑
用途适合工程制品
材料供应商佳进塑胶
密度1.42 g/cm3
硬度120
弯曲模量2830 MPa
缺口冲击强度74
热变形温度136 ℃
POM 500 美国杜邦 技术数据
性能项目试验条件[状态]测试方法测试数据数据单位
密度 ASTM D-7921.42 
吸水量浸泡均衡点+73H(+23℃)ASTM D-5700.90%
吸水量Equil.50%R.h.+73H(+23℃)ASTM D-5700.22%
挠曲系数+70℃在25℃下1585MPa
吸水量24hrs浸泡+73H(+23℃)ASTM D-5700.25%
摩擦系数+73H(+23℃)动态ThrustWasherTest30.35 
挠曲系数+23℃在25℃下2830MPa
剪力+23℃ASTM D-73265.5MPa
剪力+73HASTM D-7329.5MPsi
挠曲系数-55℃在25℃下3930MPa
洛氏硬度 ASTM D-785M94 R120 
弯曲疲劳忍耐限度+73HASTM D-6714.5MPsi
拉力冲击抵抗力+73HASTM D-1822100ft.lb/in2
扩散因数+73H(+23℃)106HzASTM D-1500.005 
伸张强度+158HASTM D-6386.9MPsi
弯曲降服强度+73HASTM D-79014.1MPsi
伸张强度+70℃ASTM D-63847.5MPa
IZOD冲击强度40℃ASDM D-25664.1j/m
伸张强度+100℃ASTM D-63835.9MPa
断裂时之拉力伸张度+73H(+23℃)ASTM D-63840%
伸张强度+212HASTM D-6385.2MPsi
断裂时之拉力伸张度+250H(+122℃)ASTM D-638>260%
压缩应力+73H@1%Def.ASTM D-6955.2MPsi
挠曲系数+158H在25℃下230MPsi
无切口冲击程度+23℃ASDM D-2561280j/m
IZOD冲击强度+23℃ASTM D-25674.7j/m
拉力冲击抵抗力+23℃ASTM D-1822200kj/m2
断裂时之拉力伸张度+212H(+100℃)ASTM D-638>260%
IZOD冲击强度+73HASDM D-2561.4ft.lb/in
压缩应力+23℃@10%Def.ASTM D-695124MPa
断裂时之拉力伸张度-68H(-55℃)ASTM D-63813%
挠曲系数+212H在25℃下90MPsi
伸张强度-68HASTM D-63814.7MPsi
熔点 ASTM D-2133175
无切口冲击程度+73HASDM D-25624ft.lb/in
弹性系数+23℃ASTM D-6383100MPa
弯曲疲劳忍耐限度+23℃ASTM D-67131.0MPa
伸张强度-55℃ASTM D-638101MPa
弹性系数+73HASTM D-638450MPsi
负载下之变形2000psi@+122H(14MPa@50℃)ASTM D-6210.5%
挠曲系数+73H在25℃下410MPsi
伸张强度+122℃ASTM D-63826.2MPa
压缩应力+23℃@1%Def.ASTM D-69535.9MPa
挠曲系数-68H在25℃下570MPsi
伸张强度+250HASTM D-6383.8MPsi
伸张强度+73HASTM D-63810.0MPsi
断裂时之拉力伸张度+158H(+70℃)ASTM D-638220%
摩擦系数+73H(+23℃)静态ThrustWasherTest30.20 
断裂时之拉力伸张度+250H(+122℃)ASTM D-638>260%
IZOD冲击强度-40HASDM D-2561.2ft.lb/in
挠曲系数+122℃在25℃下620MPa
弯曲降服强度+23℃ASTM D-79097.2MPa
压缩应力+73H@10%Def.ASTM D-69518.0MPsi
电阻系数73H(+23℃)0.2%H20ASDM D-2571015ohm-cm
电弧抵抗力120mil(3.1mm)ASTM D-495220no trackingSec.
绝缘强度Short Time 90 milsASTM D-149500V/mil
绝缘强度Short Time 2.3mmASTM D-14919.7MV/m
伸张强度+23℃ASTM D-63868.9MPa
绝缘系数+73H(+23℃)102to106HzASTM D-1503.7 
热传导系数  2.6BTU-in/hr
热传导系数  0.37W/mk
热变形温度264psiASTM D-648277H
熔点 ASTM D-2133347H
线性热膨胀系数-40 to +29℃ASTM D-69610.410-5m/m.℃
线性热膨胀系数-40 to +85HASTM D-6965.810-5in/in.H
线性热膨胀系数+104 to +150℃ASTM D-69614.910-5m/m.℃
线性热膨胀系数+220 to +300HASTM D-6968.310-5in/in.°F
热变形温度66psiASTM D-648342H
线性热膨胀系数+140 to +220HASTM D-6967.610-5in/in.°F
线性热膨胀系数+60 to +104℃ASTM D-69613.710-5m/m.℃
线性热膨胀系数+29 to +60℃ASTM D-69612.210-5m/m.℃
线性热膨胀系数+85 to +140HASTM D-6966.810-5in/in.H
热变形温度0.5MPaASTM D-648172
可燃烧性 UL-9494HB 
热变形温度1.8MPaASTM D-648136


 